3M™ Scotch® Filament Tape 890MSR

Technical Information Note

The following technical information and data should be considered representative or typical only and should not be used for speci cation purposes.

Typical Physical Properties

Property

Values

Method

Backing Color

Clear or Black

Total Tape Thickness

0.2 mm

8 mil

ASTM D3652

Backing

Polyester lm

Adhesive

Pressure sensitive modi ed synthetic

rubber resin

Reinforcement

Glass yarn

Typical Performance Characteristics

180° Peel Adhesion

Backing

Notes

Substrate

8.8 N/cm

80 oz/in

2 mil Aluminum Foil

12 in/min (300 mm/min)

72 hr dwell on Stainless Steel

88 N/100mm

Stainless Steel

Property: 180° Peel Adhesion

Method: ASTM D3330

Tensile Strength

1051 N/cm

10500 N/100mm

600 lb/in

Property: Tensile Strength

Method: ASTM D3759

Methods

ASTM D3759

Handling/Application Information

Application Techniques

An extensive line of application equipment including hand-held dispensers and an automatic L-Clip applicator is available. Application is most easily accomplished at

room temperature. At lower temperatures, approaching 32°F (0°C), the adhesive becomes rm. Once applied, Scotch® Filament Tape 890MSR performs well

throughout the normal temperature ranges encountered by packaged products in shipping and storage environments.

Storage and Shelf Life

Store behind present stock. Store in a clean, dry place. Temperature of 40-80°F (4-26°C) and 40-50% relative humidity are recommended. Rotate your stock.